Heat-resistant modified unsaturated polyester molding compound PT-310 for insulating parts
Characteristics : Heat-resistant modified unsaturated polyester molding compounds possess high resistance against electrical arc and tracking, superior mechanical strength, excellent long-term dimensional stability even at elevated temperature and good flame resistance to UL94 V-0. It has over 12 months of storage time at room temperature. PT-310 molding compounds have obtained UL certificate No. E208587.
Advantage: High proof tracking index, high resistance against electric arc, superior dielectric strength, high charpy impact strength(notched), high heat resistance and flame resistance, low water absorption, and excellent long-term dimensional stability.
Applications: Mainly used to the insulating parts for temperature controllers for household appliances, main switches, magnet coil frames, connecting terminals, low-voltage devices and flameproof devices, etc.
Technical data:
| Property | Unit | Test standard | PT-310 |
|
Density |
g/cm3 | GB/T1033 | 1.9-2.1 |
|
Water absorption |
% | GB/T1034 | ≤0.3 |
|
Moulding shrinkage |
% | JB/T3958.2 | 0.4-0.8 |
|
Charpy impact strength |
kJ/m2 | GB/T1043 | ≥6.5 |
|
Charpy notch impact strength |
kJ/m2 | GB/T1043 | ≥2.5 |
|
Flexural strength |
MPa | GB/T9341 | ≥80 |
|
Surface resistivity |
Ω | GB/T1410 | ≥1013 |
|
Volume resistivity |
Ω.m | GB/T1410 | ≥1011 |
|
Comparative tracking index (CTI) |
V | GB/T4207 | ≥600 |
|
Arc resistance |
s | GB/T1411 | ≥180 |
|
Deflection temperature |
ºC | GB/T1634 | ≥210 |
|
Flammability UL94(0.8mm) |
Level | GB/T11020 | V-0 |
|
Dielectric strength |
MV/m | GB/T1408 | ≥18.0 |
PT-310 Molding condition for injection(for reference)
|
Injection Moulding Parameters |
Unit |
Range |
|
|
Molding temperature |
ºC | 165~175 | |
|
Barrel temperature |
Feed zone |
ºC | 50~70 |
|
Nozzle zone |
ºC | 80~90 | |
|
Injection Pressure |
MPa | 60~100 | |
|
Curing time |
s/mm | 25~40 | |
|
Moulding Parameters |
Unit |
Range |
|
Molding temperature |
ºC | 165~175 |
|
Pressure |
MPa | 15~20 |
|
Curing time |
s/mm | 40~60 |